sise of billet was 9 cm in diameter about 2 cm high. the liquid state difusion(foregewelds) were don in two cicles. first the coper/brass witch binds at a higher temprature(about 895 C) then the silver/copper layers where adit. this didn't go very smooth by the way. had a lot of delamination.
maybe Ill post some more pics later. bussy at the moment.